Alkyd Ferrocyanic Anti-corrosion Coating

Alkyd iron-cloud antirust paint, alkyd iron-cloud intermediate paint, alkyd iron-cloud paint, alkyd intermediate paint, alkyd intermediate paint.

Product English name	Alkyd cloud iron anticorrosive coatings
Dangerous Goods No.	33646
UN No.	1263
Organic solvent volatility	64 standard metre³.
Brand	Jinhui Coatings
Model	C52-2-3
Colour	Grey
Mixing ratio	Single component
Appearance	Smooth surface

Alkyd iron mica anticorrosion coating is a one-component anticorrosion coating composed of alkyd resin, mica iron oxide, antirust pigment filler, additives, No.200 solvent gasoline and mixed solvents, and catalytic agent.

Status in the container: no hard lumps after stirring and mixing, in a homogeneous state.
Adhesion: first class (standard index: GB/T1720-1979(89))
Fineness: ≤60um (standard index: GB/T6753.1-2007)
Salt water resistance: 3% NaCl, 48h without cracking, blistering, peeling (standard index: GB/T9274-88)
Drying time: surface drying ≤ 5h, solid drying ≤ 24h (standard index: GB/T1728-79)

The paint film is tough, good closure, excellent anti-rust performance, can withstand the impact of temperature difference.
Strong filling ability.
Good matching performance, good combination with alkyd primer and alkyd top coat.
Good construction performance.
Strong adhesion, good mechanical properties.
High pigment content, good sanding performance.
Paint film anti-chalking, good protection performance, good light and colour retention, bright colour, good durability.

Steel surface sandblasting treatment to Sa2.5 grade, surface roughness 30um-75um.
Electrical tools descaling to St3 grade.

Suitable for steel surface, machinery surface, pipeline surface, equipment surface, wood surface.

After opening the barrel, it must be stirred evenly, left to stand, and after maturing for 30min, add appropriate amount of thinner and adjust to the construction viscosity.
Diluent: special diluent for alkyd series.
Airless spraying: Dilution amount is 0-5% (by weight ratio of paint), nozzle calibre is 0.4mm-0.5mm, spraying pressure is 20MPa-25MPa (200kg/cm²-250kg/cm²).
Air spraying: Dilution amount is 10-15% (by weight ratio of paint), nozzle calibre is 1.5mm-2.0mm, spraying pressure is 0.3MPa-0.4MPa (3kg/cm²-4kg/cm²).
Roller coating: Dilution amount is 5-10% (in terms of paint weight ratio).

Recommended film thickness	60-80um
Theoretical dosage	about 120g/m² (based on 35um dry film, excluding loss)
Recommended number of coats	2~3
Storage temperature	-10~40℃
Construction temperature	5~40℃.
Trial period	6h
Construction method	Brushing, air spraying, rolling can be.
Coating interval	Substrate temperature ℃ 5-10 15-20 25-30
	Shorter interval h 48 24 12
	The longer interval should not exceed 7 days.
Substrate temperature must be more than 3℃ above the dew point. When the substrate temperature is lower than 5℃, the paint film will not be cured and should not be constructed.

In the high temperature season construction, easy to dry spray, in order to avoid dry spray can be adjusted with thinner until not dry spray.
This product should be used by professional painting operators according to the instructions on the product package or this manual.
All coating and use of this product must be carried out in accordance with all relevant health, safety and environmental regulations and standards.
If in doubt as to whether this product should be used, please contact our technical service department for details.

The product should be stored in a cool and ventilated place, protected from direct sunlight, and isolated from sources of ignition and kept away from heat sources in a warehouse.
Products should be protected from rain, sunlight and collision when transported, and should comply with the relevant regulations of the traffic department.

The construction site should have good ventilation facilities, and painters should wear glasses, gloves, masks, etc. to avoid skin contact and inhalation of paint mist.
Smoking and fire are strictly prohibited at the construction site.